Product: 353M-12PT-54

Product Description:
A high-peel, high-tack, moderate dead load acrylic adhesive film coated on both sides of a high quality polyester film.

Product Use:
353M exhibits excellent adhesion to a very wide variety of substrates. 353M also has good general purpose foam lamination, as well as good general purpose lamination to fabricated parts. General Use: For bonding and laminating to a wide variety of urethane foams including polyether, polyester and low perm foams. For bonding and laminating to a wide variety of cloths, vinyls, corks, papers, rigid and flexible plastics.

Adhesive Family
350 Aggressive Acrylic Adhesive Tape System
Release Liner
12pt Natural Polycoated Kraft
Carrier/Backing
1/2 mil Clear Polyester Film
Tape Construction
Double Coated PET Film Tape
Adhesive Liner Side
Acrylic
Adhesive Thickness - Liner Side (Mils)
1.4
Adhesive Exposed Side
Acrylic
Adhesive Thickness - Exposed Side (Mils)
1.8
Peel Exposed Side
220 Oz/Inch

Note: Typical Values per PSTC #101 Method C, Backed with 2 Mil Aluminum Foil. 24 Hour Dwell
Peel Liner Side
210 Oz/Inch

Note: Typical Values per PSTC #101 Method C, Backed with 2 Mil Aluminum Foil. 24 Hour Dwell
Shear Exposed Side
4 days
Shear Liner Side
7 days
Service Temperature
°F to °F

Note: Data is based on limited testing and under no load.
Roll Weight
0.58 lbs/sq yards

Note: Theoretical number only. The actual roll weight may vary.
Tape Thickness (without release liner)
3.7 mils

Note: Theoretical number only. Does not include Release Liner. The actual Tape thickness may vary.
Related Products
SDS Note: If the specific product is not listed in the appendix of the provided "Article Exemption Letter", please contact your sales/account representative for a SDS.
Supplemental Peel/Shear Results
SubstrateDwell TimeTesting MethodExposed Side PeelLiner Side PeelExposed Side ShearLiner Side Shear
ABS 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 57 Oz/Inch 52 Oz/Inch 4 Days 7 Days
ABS 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 57 Oz/Inch 52 Oz/Inch 4 Days 7 Days
Materials Exposed Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 57 Oz/Inch 52 Oz/Inch 4 Days 7 Days
Materials Liner Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 57 Oz/Inch 52 Oz/Inch 4 Days 7 Days
ABS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 50 Oz/Inch 50 Oz/Inch 4 Days 7 Days
ABS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 50 Oz/Inch 50 Oz/Inch 4 Days 7 Days
Materials Exposed Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 50 Oz/Inch 50 Oz/Inch 4 Days 7 Days
Materials Liner Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 50 Oz/Inch 50 Oz/Inch 4 Days 7 Days
PLASTICS 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 40 Oz/Inch 41 Oz/Inch 4 Days 7 Days
HDPE-High Density Polyethelene 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 40 Oz/Inch 41 Oz/Inch 4 Days 7 Days
PLASTICS 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 40 Oz/Inch 41 Oz/Inch 4 Days 7 Days
Materials Exposed Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 40 Oz/Inch 41 Oz/Inch 4 Days 7 Days
HDPE-High Density Polyethelene 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 40 Oz/Inch 41 Oz/Inch 4 Days 7 Days
Materials Liner Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 40 Oz/Inch 41 Oz/Inch 4 Days 7 Days
PLASTICS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 38 Oz/Inch 42 Oz/Inch 4 Days 7 Days
HDPE-High Density Polyethelene Immediate PSTC #101 Method C, Backed with 1 mil Polyester 38 Oz/Inch 42 Oz/Inch 4 Days 7 Days
PLASTICS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 38 Oz/Inch 42 Oz/Inch 4 Days 7 Days
Materials Exposed Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 38 Oz/Inch 42 Oz/Inch 4 Days 7 Days
HDPE-High Density Polyethelene Immediate PSTC #101 Method C, Backed with 1 mil Polyester 38 Oz/Inch 42 Oz/Inch 4 Days 7 Days
Materials Liner Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 38 Oz/Inch 42 Oz/Inch 4 Days 7 Days
PP-Polypropylene 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 86 Oz/Inch 85 Oz/Inch 4 Days 7 Days
Materials Exposed Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 86 Oz/Inch 85 Oz/Inch 4 Days 7 Days
Materials Liner Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 86 Oz/Inch 85 Oz/Inch 4 Days 7 Days
PP-Polypropylene 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 86 Oz/Inch 85 Oz/Inch 4 Days 7 Days
PP-Polypropylene Immediate PSTC #101 Method C, Backed with 1 mil Polyester 75 Oz/Inch 72 Oz/Inch 4 Days 7 Days
PLASTICS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 75 Oz/Inch 72 Oz/Inch 4 Days 7 Days
PLASTICS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 75 Oz/Inch 72 Oz/Inch 4 Days 7 Days
Materials Exposed Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 75 Oz/Inch 72 Oz/Inch 4 Days 7 Days
Materials Liner Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 75 Oz/Inch 72 Oz/Inch 4 Days 7 Days
PP-Polypropylene Immediate PSTC #101 Method C, Backed with 1 mil Polyester 75 Oz/Inch 72 Oz/Inch 4 Days 7 Days
SS-Stainless Steel, Cold Rolled Steel, Unfinished Steel 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 90 Oz/Inch 84 Oz/Inch 4 Days 7 Days
METALS 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 90 Oz/Inch 84 Oz/Inch 4 Days 7 Days
SS-Stainless Steel, Cold Rolled Steel, Unfinished Steel 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 90 Oz/Inch 84 Oz/Inch 4 Days 7 Days
Materials Exposed Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 90 Oz/Inch 84 Oz/Inch 4 Days 7 Days
Materials Liner Side 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 90 Oz/Inch 84 Oz/Inch 4 Days 7 Days
METALS 24 Hours PSTC #101 Method C, Backed with 1 mil Polyester 90 Oz/Inch 84 Oz/Inch 4 Days 7 Days
SS-Stainless Steel, Cold Rolled Steel, Unfinished Steel Immediate PSTC #101 Method C, Backed with 1 mil Polyester 72 Oz/Inch 64 Oz/Inch 4 Days 7 Days
METALS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 72 Oz/Inch 64 Oz/Inch 4 Days 7 Days
SS-Stainless Steel, Cold Rolled Steel, Unfinished Steel Immediate PSTC #101 Method C, Backed with 1 mil Polyester 72 Oz/Inch 64 Oz/Inch 4 Days 7 Days
Materials Exposed Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 72 Oz/Inch 64 Oz/Inch 4 Days 7 Days
Materials Liner Side Immediate PSTC #101 Method C, Backed with 1 mil Polyester 72 Oz/Inch 64 Oz/Inch 4 Days 7 Days
METALS Immediate PSTC #101 Method C, Backed with 1 mil Polyester 72 Oz/Inch 64 Oz/Inch 4 Days 7 Days



Bonding Study Results

Manufacturer Material DescriptionBonding ResultNotes/Comments
Armacell Armacell BAJN 200 – EEA Proprietary Alloy Very Good (Foam Tear) All foam materials are laminated using heat-assisted lamination techniques and tested immediately. Results are subjective observations
Armacell Armacell BDJN 400 – EVA & PE Resin Blend Very Good (Foam Tear) All foam materials are laminated using heat-assisted lamination techniques and tested immediately. Results are subjective observations
Armacell Armacell BSJN 300 – S Grade PE Resin Very Good All foam materials are laminated using heat-assisted lamination techniques and tested immediately. Results are subjective observations
Armacell Armacell BDJN 200 – EVA & PE Resin Blend Very Good
Armacell Armacell BKJN 200 – K Grade PE Resin Very Good
Armacell Armacell BKJN 300 – K Grade PE Resin Very Good
Armacell Armacell BKJN 400 – K Grade PE Resin Very Good (Foam Tear)
Armacell Armacell BSJN 400 – S Grade PE Resin Very Good
Griswold Griswold Enlighten U Fair
Griswold Griswold Super Soft Enlighten U Good
Monarch Rubber Monarch Rubber 2055 Neprene Based Very Good All foam materials are laminated using heat-assisted lamination techniques and tested immediately. Results are subjective observations
Monarch Rubber Monarch Rubber 5013 EPDM-CR-SBR Blend Very Good (Foam Tear) All foam materials are laminated using heat-assisted lamination techniques and tested immediately. Results are subjective observations
Monarch Rubber Monarch Rubber 6071 NBR/PVC Industrial Excellent (Foam Tear) All foam materials are laminated using heat-assisted lamination techniques and tested immediately. Results are subjective observations
Monarch Rubber Monarch Rubber 3091 Pure EPDM Excellent (Foam Tear)
Monarch Rubber Monarch Rubber 4051 Epichlorohydrin Excellent (Foam Tear)
Monarch Rubber Monarch Rubber 5013 EPDM-CR-SBR Blend Excellent (Foam Tear)
Monarch Rubber Monarch Rubber 5032 EPDM-CR-SBR Blend Good



Tested Industry Specifications
Specification Type Specification Description Notes
Chrysler Chrysler PF-10770 (NC) Individual reports containing A2LA Accredited data can be provided
Ford Ford ESH-M11P19-B (3/93) Individual reports containing A2LA Accredited data can be provided
Ford Ford ESA-M11P19-A (1/79) Individual reports containing A2LA Accredited data can be provided
General Motors General Motors GM3622M (11/93) Type III Individual reports containing A2LA Accredited data can be provided
General Motors General Motors GM3622M (11/93) Type IV Cycle E Individual reports containing A2LA Accredited data can be provided
General Motors General Motors GM3607M (12/97) Type I Individual reports containing A2LA Accredited data can be provided
General Motors General Motors GM3607M (12/97) Type II Individual reports containing A2LA Accredited data can be provided
Materials Exposed Side
Materials Liner Side
Not the product you are looking for?. Need to search for something else? Click to run a new search.

Disclaimer: The above information has been provided as a general guidance to assist in preliminary identification of potential products and adhesive systems. Data presented are typical properties taken from a limited number of laboratory tests and should not be used for specification purposes. All products are sold with the understanding that purchasers will be solely responsible for determining the suitability of the materials for any purpose. Berry Global makes no warranties, either express or implied including any implied warranties of merchantability or fitness for use regarding the product information herein.

Berry Global continues to seek ways to assist you in your adhesive selections for a wide variety of materials available on the market. If we can assist you with any further testing or screening to help you select the best Adchem adhesive system or Product for your application please do not hesitate to contact our Technical Service Department or your Sales Representative.