Product Description:
A high tack, low dead load acrylic adhesive coated 1.5 mils on the exposed side of a 1/2 mil polyester film. On the user side is a 1.3 mil rubber-based adhesive, which exhibits excellent tack, high peel strength and moderate shear.
Product Use:
5944M works well with some PVC and neoprene closed cell rubber products; also with cork and rubber composites as well as with many urethane foams. This product offers the advantages of an acrylic laminating adhesive on one side of a polyester film and a synthetic rubber based adhesive on the end user's side. The polyester carrier offers excellent dimensional stability for die cutting.
GENERAL USE: This product is engineered to bond to most foams, sponges, and rubbers.
Adhesive Family
5900 Universal Foam Bonding Tape System
Release Liner
12pt Natural Polycoated Kraft
Carrier/Backing
1/2 mil Clear Polyester Film
Tape Construction
Double Coated PET Film Tape
Adhesive Liner Side
Rubber
Adhesive Thickness - Liner Side (Mils)
1.3
Adhesive Exposed Side
Acrylic
Adhesive Thickness - Exposed Side (Mils)
1.5
Peel Exposed Side
209
Oz/Inch
Note: Typical Values per PSTC #101 Method C, Backed with 2 Mil Aluminum Foil. 24 Hour Dwell
Peel Liner Side
205
Oz/Inch
Note: Typical Values per PSTC #101 Method C, Backed with 2 Mil Aluminum Foil. 24 Hour Dwell
Shear Exposed Side
10
days
Note: Typical Values per PSTC #107 (Modified) 1” x 1” x 500 gm/Sq.in. @ 72 Degree F
Shear Liner Side
7
days
Note: Typical Values per PSTC #107 (Modified) 1” x 1” x 500 gm/Sq.in. @ 72 Degree F
Service Temperature
30
°F to
150
°F
Note: Data is based on limited testing and under no load.
Roll Weight
Note: Theoretical number only. The actual roll weight may vary.
Tape Thickness (without release liner)
Note: Theoretical number only. Does not include Release Liner. The actual Tape thickness may vary.
SDS Note: If the specific product is not listed in the appendix of the provided "Article Exemption Letter", please contact your sales/account representative for a SDS.
Bonding Study Results
| Manufacturer |
Material Description | Bonding Result | Notes/Comments |
Tested Industry Specifications
| Specification Type |
Specification Description |
Notes |
| Chrysler |
Chrysler MS-CC211 Change: G |
|
|
| Delphi |
Delphi DX650017 (3/99) Type II |
|
|
|
|
|
|
|
| General Motors |
General Motors GM3622M Type I |
|
|
| General Motors |
General Motors GM3622M (11/93) Type IV Cycle E |
|
|
| General Motors |
General Motors GM3607M (12/97) Type I |
|
|