Product Description:
A high tack, high shear acrylic adhesive film coated 2.0 mils on both sides of a high quality polyester film.
Product Use:
This product was developed for use primarily for LSE bonding. The high performance Acrylic Adhesive provides bonding to a wide variety of LSE materials and foams including Urethane.
Adhesive Family
650 High Performance Acrylic Adhesive Adhesive System for LSE bonding
Release Liner
74# White Polycoated Kraft
Carrier/Backing
1/2 mil Clear Polyester Film
Tape Construction
Double Coated PET Film Tape
Adhesive Liner Side
Acrylic
Adhesive Thickness - Liner Side (Mils)
2.0
Adhesive Exposed Side
Acrylic
Adhesive Thickness - Exposed Side (Mils)
2.0
Peel Exposed Side
160
Oz/Inch
Note: Typical Values per PSTC #101 Method E, Backed with 2 Mil Aluminum Foil. 24 Hour Dwell.
Peel Liner Side
175
Oz/Inch
Note: Typical Values per PSTC #101 Method E, Backed with 2 Mil Aluminum Foil. 24 Hour Dwell.
Shear Exposed Side
7
days
Note: Typical Values per PSTC #107 Procedure A Modified, 1000 grams/Sq.Inch @ 72oF. No Dwell.
Shear Liner Side
7
days
Note: Typical Values per PSTC #107 Procedure A Modified, 1000 grams/Sq.Inch @ 72oF. No Dwell.
Service Temperature
-30
°F to
375
°F
Note: Data is based on limited testing and under no load.
Roll Weight
Note: Theoretical number only. The actual roll weight may vary.
Tape Thickness (without release liner)
Note: Theoretical number only. Does not include Release Liner. The actual Tape thickness may vary.
SDS Note: If the specific product is not listed in the appendix of the provided "Article Exemption Letter", please contact your sales/account representative for a SDS.
Bonding Study Results
Manufacturer |
Material Description | Bonding Result | Notes/Comments |